304L Stainless Steel Coil
304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition with one key difference.
Product Parameters
|
Product Name |
304L Stainless Steel Coil |
|
Type |
Steel Coil |
|
Thickness |
2.5mm-10.0mm |
|
Length |
2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. |
|
Width |
610mm-2000mm |
|
Standard |
ASTM, AISI, JIS, GB, DIN, EN, etc. |
|
Surface |
BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
|
Scope of Application |
Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
|
Certificate |
ISO, SGS, BV, etc. |
|
Production Technology |
Hot Rolling, Cold Rolling |
|
Edge Processing |
Edging, Trimming |
Chemical Composition
|
C |
Si |
Mn |
Cr |
Ni |
S |
P |
|
≤ 0.03 |
≤1.0 |
≤ 2.0 |
18.0～20.0 |
8.0～12.0 |
≤ 0.03 |
≤ 0.035 |
Mechanical Properties
|
Tensile Strength Kb (MPa) |
Yield Strength σ0.2 (MPa) |
Elongation D5 (%) |
Hardness |
|
≥ 520 |
≥ 205 |
≥ 40 |
≤ 187HB ;≤ 90HRB;≤ 200HV |
Physical Performance
|
Density(g/cm³) |
Modulus of Elasticity(Gpa) |
Coefficient of Thermal Expansion(10-6/°C) |
Coefficient of Thermal Conductivity(W/m*K) |
Resistivity(ΜΩ. cm) |
|
8.03 |
193 |
16.9 |
16.2 |
72 |
Surface Selection
Related products
-
1000kg fixed magnetic box
Contact UsSize:200mm x 97mm x 40mm
Capacity:700kgs
Net Weight:2.75kg
Material:Stainless steel and NdFeB magnet
Maximum Working Temperature:80°
Package:Carton, 300mm x 210mm x 90mm, 3pcs per carton -
China Factory 304 Stainless Steel Sheet Bright Polish 8K Grade Mirror Polished 1mm 1.5mm 2mm 3mm
Contact UsThe stainless steel plate has a smooth surface, high plasticity, toughness and mechanical strength, and is resistant to corrosion by acids, alkaline gases, solutions and other media.
-
A283/Q195 Cold Rolled Steel Coil
Contact UsA283 steel coil exhibits excellent work hardening properties during cold forming for its high strength and plasticity. After repeated cold working deformation, the coil can still show similar strength and hardness, with even better ductility and toughness. In addition, due to its good welding performance, the coil can be easily welded into parts of various shapes and sizes, and the welding quality is stable and reliable. A283 steel coils are widely used in the manufacturing of various mechanical parts, such as bolts, nuts, pins and other standard parts as well as various non-standard mechanical parts. In addition, they are also used in the manufacture of building structural materials.
-
316L Stainless Steel Plate
Contact Us316L stainless steel has a lower proportion of carbon in its composition. To qualify as 316L stainless steel, the amount of carbon cannot exceed 0.03%.
Reviews
There are no reviews yet.